Yanmayı geciktirici çeşitli kimyasal maddelerin laminat parkenin bazı özellikleri üzerine etkilerinin araştırılması

dc.contributor.advisorTutuş, Ahmet
dc.contributor.authorÖzdemir, Ferhat
dc.contributor.departmentKsü,, Fen Bilimleri Enst., Orman Endüstri Mühendisliği ABD.tr_TR
dc.date.accessioned2015-01-14T12:14:19Z
dc.date.available2015-01-14T12:14:19Z
dc.date.issued2012
dc.description.abstractBu çalışmada amaç, laminat parkenin yanmaya karşı dayanımını artırmaktır. Bu nedenle, laminat parkenin taşıyıcı panelini oluşturan yüksek yoğunlukta lif levhalar (HDF) için lif kaynağı olarak %50 kayın ve %50 sarıçam kullanılmıştır. HDF levhalar yangın geciktirici (fire retardant) kimyasal maddeler ile muamele edilerek 6.5 mm kalınlıkta üretilmiştir. Tam kuru lif miktarına oranla %3, %6, %9 oranlarında yanmayı geciktirici boraks, borik asit, amonyum polifosfat ve alfa-x kimyasalları toz halinde ilave edilmiştir. Daha sonra, HDF levhalarının yüzeyleri overlay, dekor ve balans kağıtları ile kaplanmış ve laminat parkeler üretilmiştir. Elde edilen laminat parke deneme levhalarında standartlara bağlı kalınarak fiziksel, mekanik, yüzey kalitesi özellikleri, serbest formaldehit miktarı, mantar çürüklük dayanımı ve yanma özellikleri araştırılmıştır. %3, %6 ve %9 oranlarında yanmayı geciktirici olarak ilave edilen kimyasalların, levhaların yanma dayanımını, mantar çürüklüğü ve küf mantarı dayanımını artırdığı fakat fiziksel ve mekanik direnç özelliklerini olumsuz etkilediği belirlenmiştir. Yanmayı geciktirici kimyasal maddelerin HDF levhalara ilave edilmesi ile laminat parkenin yüzey kalitesi özellikleri üzerine etkilerinin olmadığı ancak melamin emdirilmiş kağıtlara uygulanmasında ise olumsuz etki yaptığı tespit edilmiştir.tr_TR
dc.description.abstractThe aim of this study to improve the fire resistance of laminate flooring. Therefore, high density fiber boards contain mixture of 50% of Beech and 50% of Scots Pine were used for laminated flooring boards. High density fiber boards were produced using flame retardant chemicals with the thickness of 6.5 mm. Fire retardants such as borax, boric acid, ammonium polyphosphate and alpha-x-chemicals were added in the powder form with the concentration of 3%, 6% and 9% of dry fiber weight. Afterwards, surfaces of HDF boards were coated with overlay, decor and balance sheets and then laminated floorings boards were produced. The physical, mechanical, surface properties, amounts of free formaldehyde, resistance of fungal decay and fire resistance of all produced laminated flooring samples were investigated in accordance to relevant standarts. Addition of fire retardant chemicals such as borax, boric acid, ammoniumpolyfosfat and alfa-x,were at 3%, 6% and 9% proportions improved the fire resistance, fungal decay and mold resistance but had a negative effect on both the physical and mechanical properties. It was also detectedthat the internal addition of fire retardant chemicals had no negative effects on the surface quality of HDF boards whereas the application of such chemicals on the melamineimpregnated papers had destructive effects on the surface properties of tested samplestr_TR
dc.identifier.endpage218tr_TR
dc.identifier.startpageXVIII,1tr_TR
dc.identifier.urihttps://acikerisim.ksu.edu.tr/handle/ksu/276
dc.language.isoturtr_TR
dc.publisherFerhat Özdemirtr_TR
dc.subjectBorik asit, Boraks, Alfa-X, Laminat Parke, Yanmatr_TR
dc.subjectBoric acid, Borax, Alfa-X, Laminate Flooring, Combustiontr_TR
dc.titleYanmayı geciktirici çeşitli kimyasal maddelerin laminat parkenin bazı özellikleri üzerine etkilerinin araştırılmasıtr_TR
dc.typedoctoralThesistr_TR

Files

Original bundle
Now showing 1 - 1 of 1
Loading...
Thumbnail Image
Name:
T01687.pdf
Size:
15.42 MB
Format:
Adobe Portable Document Format
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description: